    2. EN 10269 Grade X6NiCrTiMoVB25-15-2 (1.4980)

    EN 10269 Grade X6NiCrTiMoVB25-15-2 (1.4980) Fasteners

    Precipitation-Hardened Austenitic Stainless Steel Bolts, Stud Bolts, Screws, Nuts & Washers in EN 10269 Grade X6NiCrTiMoVB25-15-2 (1.4980)

    EN 10269 Grade X6NiCrTiMoVB25-15-2 (1.4980) Fasteners are precipitation-hardened austenitic stainless steel fasteners equivalent to A-286, offering very high tensile strength, excellent creep resistance, and oxidation resistance at temperatures up to 700°C, used in gas turbine bolting, jet engine components, and critical high-temperature pressure vessel applications.

    EN 10269 X6NiCrTiMoVB25-15-2 Chemical composition

    Material designation Chemical composition, % by mass
    Name Number C Si Mn P max. S max. Al tot B Cr Mo Ni V Others
    Steels for quenching and tempering
    X6NiCrTiMoVB25-15- 2 1.4980 0,03 to 0,08 ≤ 1,00 1,00 to 2,00 0.025 0.015 ≤ 0,35 0,003 0 to 0,010 13,5 to 16,0 1,00 to 1,50 24,0 to 27,0 0,10 to 0,50 Ti: 1,90 to 2,30
    • a Elements not listed in this table may not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All appropriate precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the usefulness of the steel.
    • b A controlled sulphur content of 0,015 % to 0,030 % improves the machinability and is therefore recommended and may be agreed at time of enquiry and order. For weldability, a controlled sulphur content of 0,008 % to 0,030 % is recommended and may be agreed at time of enquiry and order.
    • c For requirements regarding magnetic properties up to a maximum of 0,28 % C.

    EN 10269 X6NiCrTiMoVB25-15-2 Mechanical properties

    EN 10269 X6NiCrTiMoVB25-15-2 Proof strength

    Minimum 0,2 %-proof strength values at elevated temperature of steels in delivery conditions which support the Essential Safety Requirements of Directive 97/23/EC d

    Material designation Heat treatment conditiona Diameter e d mm Minimum 0,2 %-proof strength Rp0,
    2 in MPa at a temperature (in °C) of:
    Name Number 50 100 150 200 250 300 350 400 450 500 550 600 650
    X6NiCrTiMoVB25-15-2 1.4980 +AT+P d ≤ 160 592*) 580 570 560 550 540 530 520 510 490 460 430 380
    • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened; +QT = quenched and tempered; +WW = warm worked (see Annex B).
    • b This steel grade is generally not applied in the creep range.
    • c Values in brackets signify that the steel is not intended for use (and testing) at those temperatures.
    • d Products made to these steel grades and these final heat treatment conditions support the Essential Safety Requirements of Directive 97/23/EC; see Annex 1, 7.5 of this directive.
    • e For rectangular cross sections "d" will be replaced by "b" (see Figure 1).
    • *) Values calculated by linear interpolation.

    EN 10269 X6NiCrTiMoVB25-15-2 Tensile Strength

    Minimum tensile strength values at elevated temperatures of steels in delivery conditions which support the Essential Safety Requirements of Directive 97/23/EC b

    Material designation Heat treatment conditiona Diameter c d mm Minimum tensile strength Rm
    in MPa at a temperature (in °C) of:
    Name Number 50 100 150 200 250 300 350 400 450 500 550 600 650
    X6NiCrTiMoVB25-15-2 1.4980 +AT+P d ≤ 160 - - - - - - - 720 710 700 690 670 -
    • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened; +QT = quenched and tempered; +WW = warm worked (see Annex B).
    • b Products made to these steel grades and these final heat treatment conditions support the Essential Safety Requirements of Directive 97/23/EC; see Annex 1, 7.5 of this directive.
    • c For rectangular cross-sections "d" will be replaced by "b"

    EN 10269 X6NiCrTiMoVB25-15-2 Impact Energy

    Minimum impact energy (longitudinal direction) at low temperature of steels in delivery conditions which support the Essential Safety Requirements of Directive 97/23/EC b

    Material designation Heat treatment conditiona Diameter e d mm Minimum impact energy KV2 in J c
    (ISO-V test piece) at a test temperature in °C of:
    Name Number -270 -196 -160 -140 -120 -110 -100 -90 -80 -70 -60 -50 -40 -20 0 +20
    • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened; +QT = quenched and tempered; +WW = warm worked (see Annex B).
    • b Products made to these steel grades and these final heat treatment conditions support the Essential Safety Requirements of Directive 97/23/EC; see Annex 1, 7.5 of this directive.
    • c Average of 3 test results.
    • d Steel grade 1.4980 may be ordered for cryogenic purposes with impact values of 50 J at -270 °C, 60 J at -196 °C and 70 J at 20 °C.
    • e For rectangular cross sections "d" will be replaced by "b"
    Specifications
    Surface Treatments
    Certifications
    About Us
    Questions? Contact us.
    Showcase of our Microsites.
    Satisfaction Survey

    survey

    TUVRheinland CRETIFIED

    © TorqBolt P(Ltd) · Built with in INDIA.