    2. EN 10269 Grade C35E (1.1181)

    EN 10269 Grade C35E (1.1181) Fasteners

    Medium-Carbon Steel Bolts, Stud Bolts, Screws, Nuts & Washers in EN 10269 Grade C35E (1.1181)

    EN 10269 Grade C35E (1.1181) Fasteners are medium-carbon steel fasteners with good mechanical properties and machinability, commonly used for bolting in pressure vessels, heat exchangers, and general industrial applications at elevated temperatures.

    EN 10269 C35E Chemical composition

    Material designation Chemical composition, % by mass
    Name Number C Si Mn P max. S max. Al tot B Cr Mo Ni V Others
    Steels for quenching and tempering
    C35E 1.1181 0,32 to 0,39 ≤ 0,40 0,50 to 0,80 0.030 0,015 b - - ≤ 0,40 ≤ 0,10 ≤ 0,40 - Cr+Mo+Ni: ≤ 0,63
    • a Elements not listed in this table may not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All appropriate precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the usefulness of the steel.
    • b A controlled sulphur content of 0,015 % to 0,030 % improves the machinability and is therefore recommended and may be agreed at time of enquiry and order. For weldability, a controlled sulphur content of 0,008 % to 0,030 % is recommended and may be agreed at time of enquiry and order.
    • c For requirements regarding magnetic properties up to a maximum of 0,28 % C.

    EN 10269 C35E Mechanical properties

    Mechanical properties at Room Temperature

    Mechanical properties at room temperature and at 20 °C of steels in delivery conditions which support the Essential Safety Requirements of Directive 97/23/ECb

    Material designation Heat treatment conditiona Diameter c Proof strength Tensile strength Elongation after fracture Reduction in area Impact energy (ISO-V) at 20°C
    Name Number
    d mm Rp0,2 MPa min. Rm MPa A % min. Z % min. KV2 J min.
    C35E 1.1181 +N d ≤ 60 300 500 to 650 20 - 27
    • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened;
    • +QT = quenched and tempered; +WW = warm worked (see Annex B).
    • b Products made of steel grades and these final heat treatment conditions support the Essential Safety Requirements of Directive 97/23/EC, see Annex 1, 7.5 of this directive.
    • c For rectangular cross-sections "d" will be replaced by "b" (see Figure 1).

    EN 10269 C35E Proof strength

    Minimum 0,2 %-proof strength values at elevated temperature of steels in delivery conditions which support the Essential Safety Requirements of Directive 97/23/EC d

    Material designation Heat treatment conditiona Diameter e d mm Minimum 0,2 %-proof strength Rp0,
    2 in MPa at a temperature (in °C) of:
    Name Number 50 100 150 200 250 300 350 400 450 500 550 600 650
    C35E 1.1181 +N d ≤ 60 289*) 270*) 251 229 213 192 182 173 - - - - -
    • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened; +QT = quenched and tempered; +WW = warm worked (see Annex B).
    • b This steel grade is generally not applied in the creep range.
    • c Values in brackets signify that the steel is not intended for use (and testing) at those temperatures.
    • d Products made to these steel grades and these final heat treatment conditions support the Essential Safety Requirements of Directive 97/23/EC; see Annex 1, 7.5 of this directive.
    • e For rectangular cross sections "d" will be replaced by "b" (see Figure 1).
    • *) Values calculated by linear interpolation.
    Specifications
    Surface Treatments
    Certifications
    About Us
    Questions? Contact us.
    Showcase of our Microsites.
    Satisfaction Survey

    survey

    TUVRheinland CRETIFIED

    © TorqBolt P(Ltd) · Built with in INDIA.